The salt spray (or salt fog) test is a standardized and popular corrosion test method, used to ASTM B was the first internationally recognized salt spray standard, originally published in Other important relevant standards are. Designation: B – 07a Standard Practice for Operating Salt Spray (Fog) Apparatus1 This standard is issued under the?xed designation B. ASTM B Testing, also known as a Standard Practice for Operating Salt ASTM B Testing requires controls over many operational parameters such as: .

Author: Kigabei Akinoktilar
Country: Bulgaria
Language: English (Spanish)
Genre: Art
Published (Last): 4 April 2012
Pages: 211
PDF File Size: 17.13 Mb
ePub File Size: 1.54 Mb
ISBN: 255-7-46966-960-8
Downloads: 90237
Price: Free* [*Free Regsitration Required]
Uploader: Kazizuru

The most commonly used type is made of plastic. Place the panels in the proximity of the condensate collectors.

SAL 400-FL

Hot-dip galvanizing produces zinc carbonates when exposed to a natural environment, thus protecting the coating metal and reducing the corrosion rate. The pH measurement shall be made as described in 8.

Construction of a plastic nozzle, such as is furnished by several suppliers, is shown in Fig.

The number of cycle repeats and therefore the test duration is variable. Test solution b11707a L. Please find more details at www. The temperature within the exposure zone of the closed axtm shall be recorded Note 8 at least once daily except on Saturdays, Sundays, and holidays when the salt spray test is not interrupted for exposing, rearranging, or removing test specimens or to check and replenish the solution in the reservoir NOTE 8—A suitable method to record the temperature is by a continuous recording device or by a asstm which can be read from outside the closed cabinet.

This test can be used to test the relative resistance to corrosion of aluminium alloys when exposed to a changing climate of acetic acid salt spray, followed by air drying, followed by high humidity, all at an elevated temperature. A solution that requires between 3. Cyclic corrosion testing is better suited to this.

Suitably located and directed spray nozzles avoid ceiling accumulation and drip. Test specimens are ashm in an enclosed chamber, and exposed to 1 of 2 possible changing climate cycles. Retrieved from ” https: B Ast, order to ensure that the proper salt concentration was achieved when mixing the solution, it is recommended that the solution be checked with either a salimeter hydrometer or speci?

  EHD 60020 P PDF

Corrosion tests and standards: The values given in parentheses are for information only. The first prerequisite for your test chamber to operate properly is that it is regularly serviced and well maintained.

SaliCORR® ASTM B Sodium Chloride

b117-07aa Although popular in certain industries, modified salt spray testing has in many cases been superseded by Cyclic corrosion testing CCT The type of environmental test chambers used for modified salt spray testing to ASTM G85 are generally similar to adtm chambers used for testing to ASTM Bbut will often have some additional features, such as an automatic climate cycling control system.

The chamber has the following features: Qstm cleaning method shall be optional depending on the nature of the surface and the contaminants.

The appearance of corrosion products rust or other oxides is evaluated after a pre-determined period of time. Painted surfaces with an underlying hot-dip galvanized coating can be tested according to this method. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM International Headquarters.

SAL 3000-FL

The fallout rate should be measured for 16 hours and it must range from 1. Position of Specimens During Exposure 7.

Suitable apparatus which may be used is described in Appendix X1. ASTM G85 annex A1 — Acetic Acid Salt Spray Test non-cyclic This test can be used to determine the relative resistance to corrosion of decorative chromium plating on steel and zinc based die casting when exposed to an acetic acid salt spray climate at an elevated temperature. Test solution tank L complete with tankfilter,hose and fitting.

ASTM B – 07a Standard Practice for Operating Salt Spray (Fog) Apparatus

Testing cabinets are manufactured according to the specified requirements here. Chamber volumes vary from supplier to supplier.

The first prerequisite for your test chamber to operate properly is that it is regularly serviced and well maintained. Current edition approved Dec. Slotted wooden strips are suitable for the support of? Most commonly, the time taken for oxides to appear on the samples under test is compared to expectations, to determine whether the test is passed or failed.

  HANS FRYBA SUITE PDF

In the automotive industry requirements are specified under material specifications. atm

There is a general historical consensus that larger chambers can provide a more homogeneous testing environment. Regarding any new applications, it is essential to correlate the results of this practice aztm actual?

Individual reprints single or multiple copies of this standard may be obtained by contacting ASTM at the above address or at phonefaxor service astm.

How can I check whether my salt spray test chamber operates properly?

For this reason the salt spray test is most often deployed in a quality audit role, where, for example, it can be used to check the effectiveness of a production process, such as the surface coating of a metallic part. Take about a mL sample of the salt solution as prepared at room temperature, boil gently for 30 s, cool, and determine the pH. This test is also referred to as an ASS test. Such tests are commonly referred to as modified salt spray tests. When the pH of the salt solution is adjusted to 6.

Position the collectors in the proximity of the test specimens, one nearest to any nozzle and the other farthest from all nozzles. Salt Spray Test Chambers. NOTE 2—Suitable materials for the construction or coating of racks and supports are glass, rubber, plastic, or suitably coated wood.

Continuity of Exposure Continuous operation implies that the chamber be closed and the spray operating continuously except for the short daily interruptions necessary to inspect, rearrange, or remove test specimens, to check and replenish the solution in the reservoir, and to make necessary recordings as described in Section The first climate cycle comprises a continuous indirect spray of neutral pH 6. These standards describe the necessary information to carry out this test; testing parameters such as temperature, air pressure of the sprayed solution, preparation of the spraying solution, concentration, pHetc.